NATURESIN🍀BY RESINPRO®
Mineral resicing on the water base
The product is perfect for creating trays, cup trays, ashtrays, plates, jewelry boxes, flowerpots, cutting boards, candle holders, mobile phone holders and various household and office items!
The product is also suitable for a variety of casting and lamination activities, including decorative items, rubber mold counterforms, polystyrene and foam coatings, rigid forms and many other applications in the mold sector.
NatuResin🍀is suitable for indoor and outdoor use.
However, in the external environment, in order to maintain the appearance of surfaces, it is recommended to use the product in combination with a protective agent.
PREPARATION
To ensure compliance with the specifications of the material, it is important to consider the components with precision scales and the blender supplied by us. Ignoring these guidelines can lead to a decrease in strength, slower hardening and reduced durability. The workshop environment must be sufficiently heated, moisture-free and protected from direct sunlight. Avoid environments where solvent-based compounds are regularly used. The containers used for mixing must be clean, dry and of sufficient size.
MIXING RATIO
Guide:
– White single-component 100:27 (powder: water)
Dust component: water 100:27 (by weight)
Catalysis time: 40 ′
white color
N.B .: It is possible to change the mixing ratio with mineral or metal fillers, adding sands, light fillers, etc.
For more information, see the instructions below.
MIXING
Prepare a large container to accommodate two components.
Add liquid to the container in the desired doses.
Add the base powder component (pre-weighted according to the usage ratio) to the liquid little by little by little.
When the entire base powder component is added, continue to mix the mixture until a homogeneous, liquid and lumpless mixture is obtained.
The workable time limit at the standard ratio is 12-15 minutes.
When natu🍀Resin mixture is poured into the mold, then to facilitate the exit of air bubbles from the mixture, the form of the cloacas a couple of times strongly against the supporting surface.